Mixture of tin + Bismuth + copper

Datasets

1. Excess molar enthalpy (molar enthalpy

Excess molar enthalpy (molar enthalpy of mixing), kJ/mol [ref]

Operational conditions:

• Pressure, kPa = 101 (Liquid)
• Temperature, K = 1073.2 (Liquid)

Fixed		Measured
Mole fraction of Bismuth (2) - Liquid	Mole fraction of copper (3) - Liquid	Excess molar enthalpy (molar enthalpy of mixing), kJ/mol - Liquid
0.0313	0.6871	-4.467
0.0323	0.6767	-4.303
0.0334	0.6656	-4.137
0.0346	0.6537	-3.952
0.0359	0.6411	-3.764
0.0372	0.6277	-3.562
0.0386	0.6136	-3.371
0.0401	0.5986	-3.152
0.0417	0.5828	-2.93
0.0434	0.5658	-2.687
0.0452	0.5477	-2.44
0.0472	0.5280	-2.186
0.0493	0.5066	-1.921
0.0517	0.4831	-1.651
0.0542	0.4577	-1.377
0.0570	0.4297	-1.12
0.0601	0.3990	-0.8700
0.0635	0.3650	-0.6230
0.0673	0.3269	-0.3900
0.0716	0.2842	-0.1710
0.0763	0.2373	-0.0010
0.0815	0.1851	0.1250
0.0815	0.6737	-3.376
0.0820	0.6717	-3.031
0.0841	0.6633	-3.178
0.0846	0.6611	-2.821
0.0867	0.6526	-2.974
0.0874	0.1256	0.1900
0.0874	0.6500	-2.601
0.0895	0.6415	-2.766
0.0903	0.6382	-2.402
0.0913	0.7231	-3.785
0.0924	0.6299	-2.605
0.0935	0.6256	-2.228
0.0936	0.0635	0.1600
0.0944	0.7138	-3.732
0.0954	0.6177	-2.447
0.0969	0.6121	-2.039
0.0976	0.7039	-3.661
0.0987	0.6048	-2.274
0.1005	0.5976	-1.847
0.1011	0.6934	-3.546
0.1021	0.5910	-2.088
0.1043	0.5824	-1.65
0.1048	0.6822	-3.404
0.1058	0.5763	-1.89
0.1083	0.5664	-1.451
0.1087	0.6703	-3.229
0.1097	0.5605	-1.69
0.1126	0.5492	-1.239
0.1129	0.6577	-3.015
0.1140	0.5435	-1.48
0.1172	0.5307	-1.035
0.1173	0.6442	-2.765
0.1185	0.5251	-1.265
0.1221	0.5112	-0.8330
0.1221	0.6298	-2.468
0.1235	0.5053	-1.058
0.1272	0.6142	-2.168
0.1273	0.4902	-0.6250
0.1289	0.4837	-0.8360
0.1328	0.5972	-1.804
0.1329	0.4678	-0.4190
0.1347	0.4605	-0.6270
0.1389	0.4437	-0.2150
0.1389	0.5787	-1.449
0.1410	0.4353	-0.4150
0.1454	0.4179	-0.0280
0.1455	0.7084	-2.651
0.1456	0.5585	-1.11
0.1458	0.7085	-2.556
0.1478	0.4080	-0.2190
0.1504	0.6985	-2.67
0.1505	0.6990	-2.566
0.1524	0.3898	0.1630
0.1528	0.5364	-0.8240
0.1551	0.3786	-0.0260
0.1554	0.6885	-2.68
0.1555	0.6890	-2.574
0.1599	0.3599	0.3340
0.1607	0.6778	-2.661
0.1609	0.5121	-0.5540
0.1631	0.3465	0.1620
0.1663	0.6667	-2.624
0.1664	0.6672	-2.517
0.1681	0.3270	0.4740
0.1696	0.4856	-0.2770
0.1719	0.3113	0.3140
0.1722	0.6547	-2.566
0.1724	0.6554	-2.458
0.1769	0.2915	0.5860
0.1786	0.6419	-2.469
0.1787	0.6428	-2.352
0.1793	0.4561	-0.0090
0.1816	0.2724	0.4500
0.1854	0.6292	-2.217
0.1855	0.6282	-2.323
0.1865	0.2533	0.6600
0.1902	0.4233	0.2510
0.1924	0.2292	0.5160
0.1926	0.6148	-2.06
0.1929	0.6133	-2.136
0.1969	0.2117	0.7000
0.2004	0.5992	-1.84
0.2009	0.5972	-1.925
0.2020	0.3873	0.4940
0.2045	0.1809	0.5470
0.2077	0.6850	-0.7990
0.2080	0.1671	0.6670
0.2088	0.5826	-1.588
0.2094	0.5802	-1.646
0.2146	0.6745	-0.8950
0.2149	0.3482	0.6960
0.2178	0.1276	0.4980
0.2178	0.5645	-1.302
0.2185	0.5621	-1.337
0.2203	0.1178	0.5840
0.2220	0.6633	-0.9750
0.2276	0.5449	-0.9350
0.2283	0.5424	-0.9550
0.2290	0.3056	0.8510
0.2298	0.6514	-1.034
0.2327	0.0679	0.3600
0.2342	0.0623	0.3960
0.2381	0.6388	-1.089
0.2383	0.5234	-0.5350
0.2390	0.5209	-0.5410
0.2442	0.2595	0.9460
0.2468	0.6687	0.1820
0.2470	0.6254	-1.111
0.2497	0.6668	0.7090
0.2500	0.5000	-0.0250
0.2506	0.4976	-0.0550
0.2564	0.6559	0.2180
0.2565	0.6110	-1.097
0.2585	0.6550	0.6940
0.2614	0.2071	0.9410
0.2629	0.4744	0.4890
0.2633	0.4721	0.4240
0.2664	0.5959	-1.066
0.2666	0.6422	0.2500
0.2679	0.6424	0.5930
0.2720	0.6978	-0.1510
0.2765	0.6289	0.2860
0.2770	0.4462	0.8420
0.2770	0.5798	-0.9980
0.2774	0.4439	0.7490
0.2780	0.6289	0.5230
0.2812	0.1472	0.8330
0.2817	0.6870	-0.1330
0.2871	0.6147	0.3240
0.2884	0.5625	-0.9040
0.2888	0.6146	0.4520
0.2917	0.6758	-0.1180
0.2924	0.4154	1.12
0.2930	0.4127	1.036
0.2984	0.5995	0.3620
0.3002	0.5993	0.4010
0.3004	0.5444	-0.7670
0.3024	0.6639	-0.1030
0.3041	0.0778	0.5650
0.3092	0.3819	1.324
0.3101	0.3783	1.239
0.3104	0.5834	0.4090
0.3121	0.5835	0.3630
0.3134	0.5246	-0.5820
0.3138	0.6513	-0.0890
0.3229	0.5666	0.4600
0.3249	0.5664	0.3910
0.3259	0.6378	-0.0770
0.3275	0.5032	-0.3360
0.3277	0.3447	1.498
0.3293	0.3399	1.418
0.3360	0.5491	0.5020
0.3386	0.5481	0.4190
0.3387	0.6236	-0.0580
0.3429	0.4798	-0.0130
0.3483	0.3035	1.604
0.3499	0.5304	0.5530
0.3502	0.2980	1.526
0.3522	0.6086	-0.0270
0.3533	0.5284	0.4870
0.3598	0.4543	0.3790
0.3649	0.5103	0.6120
0.3664	0.5928	0.0070
0.3690	0.5075	0.6110
0.3715	0.2572	1.614
0.3737	0.2508	1.563
0.3783	0.4261	0.8560
0.3811	0.4885	0.7100
0.3819	0.5756	0.0560
0.3860	0.4848	0.7760
0.3977	0.2048	1.515
0.3983	0.4655	0.7970
0.3986	0.5571	0.0880
0.3989	0.3949	1.426
0.3993	0.1995	1.47
0.4044	0.4602	1.001
0.4167	0.5369	0.1270
0.4170	0.4403	0.9020
0.4198	0.5344	2.912
0.4216	0.3605	1.983
0.4247	0.4333	1.301
0.4277	0.1448	1.27
0.4285	0.1411	1.229
0.4361	0.4146	1.007
0.4363	0.5152	0.1660
0.4394	0.5128	3.091
0.4407	0.5120	3.721
0.4450	0.4061	1.673
0.4468	0.3222	2.21
0.4567	0.3870	1.103
0.4573	0.4918	0.2170
0.4605	0.4893	3.173
0.4614	0.0775	0.8120
0.4615	0.0747	0.7850
0.4640	0.4862	3.802
0.4673	0.3763	2.082
0.4751	0.2794	2.225
0.4789	0.3573	1.241
0.4796	0.4670	0.2810
0.4837	0.4636	3.247
0.4897	0.4578	3.858
0.4914	0.3441	2.565
0.5023	0.3259	1.387
0.5041	0.4398	0.3460
0.5060	0.2325	2.135
0.5089	0.4357	3.328
0.5179	0.3088	2.827
0.5179	0.4265	3.932
0.5269	0.2928	1.55
0.5311	0.4098	0.4240
0.5365	0.4051	3.396
0.5385	0.1832	1.911
0.5473	0.2696	2.804
0.5489	0.3922	3.933
0.5513	0.2600	1.739
0.5602	0.3774	0.5200
0.5672	0.3710	3.436
0.5747	0.1282	1.522
0.5802	0.2257	2.618
0.5831	0.3544	3.917
0.5920	0.3421	0.6170
0.6016	0.3329	3.411
0.6036	0.1899	2.155
0.6153	0.0667	0.9300
0.6163	0.1775	2.304
0.6212	0.3121	3.801
0.6347	0.1482	2.429
0.6403	0.2900	3.309
0.6561	0.1244	1.782
0.6591	0.2675	0.8410
0.6646	0.2641	3.564
0.6690	0.1020	2.761
0.6833	0.2423	3.074
0.6991	0.2231	0.9770
0.7004	0.0652	1.059
0.7056	0.0530	3.181
0.7131	0.2103	3.13
0.7312	0.1892	2.643
0.7425	0.1749	1.127
0.7686	0.1489	2.467
0.7824	0.1325	2.061
0.7913	0.1207	1.333
0.8332	0.0773	1.445
0.8401	0.0684	1.18
0.8462	0.0596	1.586

Sources

• Enthalpies of mixing of liquid Bi Cu and Bi Cu Sn alloys relevant for lead-free soldering